PMMA Injection Molding Process
PMMA Injection Molding Process
Acrylic, its chemically name called polymethyl methacrylate (PMMA in English). Due to the shortcomings of PMMA surface hardness is low, easy to scratch, low impact resistance, poor molding fluidity, etc., the modification of PMMA has appeared one after another. Such as the copolymerization of methyl methacrylate with styrene and butadiene, the blending of PMMA and PC and so on.
The flow of PMMA is worse than PS and ABS, and the melt viscosity is more sensitive to temperature changes. During the molding process, the melt viscosity is mainly changed from the injection temperature. PMMA is an amorphous polymer with a melting temperature greater than 160°C and a decomposition temperature of 270°C.
1. Plastic processing
PMMA has a certain degree of water absorption, with a water absorption rate of 0.3-0.4%, and injection molding must have a humidity below 0.1%, usually 0.04%. The presence of water causes bubbles, gas lines, and reduced transparency in the melt. So it needs to be dried. The drying temperature is 80-90℃, and the time is more than 3 hours. Recycled materials can be used 100% in some cases. The actual amount depends on the quality requirements, usually over 30%. Recycled materials should avoid pollution, otherwise it will affect the transparency and the properties of the finished product.
2. Injection machine choose
PMMA has no special requirements for injection molding machines. Because of its high melt viscosity, a deeper screw groove and a larger diameter nozzle hole are required. If the strength of the product is higher, a screw with a larger length to diameter ratio should be used for low-temperature plasticization. In addition, PMMA must be stored in a dry hopper.
3. Mold and gate design
The mold temperature can be 60℃-80℃, the diameter of the sprue should match the inner taper, the best angle is 5° to 7°, if you want to inject 4mm or more , the angle should be 7°, and the diameter of the sprue can reach 8 to 10mm, the overall length of the gate should not exceed 50mm. For products with a wall thickness of less than 4mm, the diameter of the runner should be 6-8mm. For products with wall thickness greater than 4mm, the runner diameter should be 8-12mm. Diagonal, fan-shaped and tabular gate depth should be 0.7 to 0.9t (t is the thickness of the product wall), and the diameter of the needle gate should be 0.8 to 2mm; smaller size should be used for low viscosity.
The common vent holes have a depth of less than 0.05 and a width of 6mm. The demolding angle is between 30'-1° and 35'-1°30° in the cavity part.
4. Melting temperature
It can be measured by air injection method: ranging from 210°C to 270°C, depending on the information provided by the supplier.
Withdraw the back seat, make the nozzle of the injection molding machine leave the sprue bushing, and then manually perform plasticization injection molding, which is air injection molding.
5. Inject Temperature
Fast injection can be used, but to avoid high internal stress, it is advisable to use multi-stage injection, such as slow-fast-slow, etc. When injecting thick parts, use slow speed.
6. Residence time
If the temperature is 260℃, the residence time should not exceed 10 minutes, if the temperature is 270℃, the residence time should not exceed 8 minutes.
TAGS : molding injection molding mold